Denim Garments Lycra Problems Resolve Solutions- Textile Farm

Causes and Remedies for Garment  Lycra Denim.

We have a common problem for those who have oven dyeing Wasting. After the garments Spandex Damage, Spandex or Lycra Damage, the shipment is not canceled, the amount of wasting plant is less. You are the Garment's WAS expert, you need to have ideas on who or what you are careful about.

Lycra Denim Fabric

I can comment if there is something out of Lycra Damage in my mind
1. The enzymes that hydrolyze or break the cellulose fiber can break the fiber twist if biodegradation by enzymes that break Lycra due to excess pressure on Lycra, because of the Betting Actions of War Machine.
2. If there is a fiber or break due to the machine's firing in the fiber or the card or the rotatory, Lycra can be broken due to the weakness of the twist.
3. If the lycra blends fabric or garment is heavy, then it will be rubbed with a rubber ball or a stone without enzymes of its look. To avoid damages, it is best not to the enzyme.
4. If the Lycra Blend fabric or garment dyeing or washer program is to be used, then pitch dyeing machine should be used. It does not contain much of the locker volume and the machine cylinder does not contain the battery, it turns the pedal locker at the top position of the machine so that due to low body-to-body biting, there is less body damage than you can. Betting Action Front loading (Tonello, Ramsons), Bailey Machine (China) machine is much more than the beating pitch diving machine.
5. Special Lycra Protector should be used, which is not a generic or Anti-Sleeping Agent. A typical recipe for this is 15 gram per liter, which is 2 gram per liter in the factory.

Lycra Garments

6. Anti-slipping agents with anti-cruising 0.5 g, sewing assistants 0.5 g of 0.5 g waiting agent to use. Which is not followed much time.

7. When Hydro is extracted, it is found in the fact that the load is loaded on the back of the load condition. Load condition is due to the centrifugal force, due to body twisting, there is a Lycra denim's choice. Therefore, the reduction in loading of the screws of Lycra bodies will be reduced. And the speed RPM should be reduced so that the centrifugal force is less affected.

8. 50-60% Hydro and Warming Curving Machine, and the need to drive in the steam dryer. This will cause less stress on the Lycra Blend body.

9. Horizontal or Bailey Me shim Vertical Front loading Machine Betting of the body can be damaged by machine RPM. Less than 30 RPM It can be run on machine-to-body bits less than one.

10. M: L 1: 8, 1: 6, 1:10 The scope of Lycra should be run at 1:30 am in M: L, but the amount of chemical weight is higher than body damage.

11. Hydro time for one piece, where 75 seconds can extract extracting time in Lycra body, such as 45 seconds.
The area of 12 zippers should be changed after the per-processions such as during the time of discoloration, occasionally during the time of sublingual, after changing the position of the zipper after each process, there is a possibility of stress in one place and if there is a stress, then there is a possibility of going to the ground. The time of bleeding should be kept open during bleach.

13. If the access barter stitch pocket belt is in the area of the loop, it is more than the pressure of the pressure or the bar tech stitch on the back pocket side, due to which there is more tendency to avoid despondency outside of the stitch area.

14. Garment Allowance is uninstalled, for which it will be parked in the body. Body Damage is more due to Gathering
.
15. During the swing, many operators have dragged and swindled with tension, which means that Lycra took the Inside Tension, which later broke the heat on the Garments Watt and machine bits.

16. If the cutting blade is less in the cutting time, then during the fabric cutting, the core filaments are drawn from the interstitial condition of the tension.

17. Generally, if the widest width of the Oven Fabric Finnish is more than the widest, then the Lycra Damage is broken and the illness decreases. During the hit setting, it will be better to set the hit. Oven Fabric Finnish width should be 52-53 ".

18. Dryer selections should be selected by our stem dryer. Lycra blend body cuts the steam dryer in the wound slowly and the temperature is inevitable, which does not have a bad effect on the body. Tempe re is less so damaged by low, our gas dryer should be avoided by the moisture content. The Temperature Control cannot be controlled.

20. Must use caustic soda when blemishes are attached to the Denim Lycra Fabric.

21. For Lycra Fabric, you need to have 45 min 60 ° C dryer and  Lycra fabric for 35 min 80 ° C dryer.